PA12 CF

Fiber Fibra de carbono rígida y resistente

Compatibility:

PRO

BigRep's PA12-CF is a strong and heat-resistant engineering-grade filament with a great surface finish. PA12-CF is stiff, durable, and perfect for a wide range of professional tooling applications for many industries. With good chemical resistance, PA12-CF parts typically don't require additional post-processing to withstand the demands of industrial use. Just 3D print and immediately use your parts.

Reinforced with 10% chopped carbon fibers, BigRep PA12-CF is ideal for functional applications usually produced with ABS - such as jigs, fixtures, grippers, or end-of-arm parts - because it is suitable for long-term stress, and shows good resistance and durability for daily production usage.

A reliable and easy-to-use engineering performance material, BigRep PA12-CF is optimized for large-format 3D printing and suitable for demanding environments, such as factory floors.

HIGHLIGHTS:

Stiff and durable parts
High Heat Deflection Temperature (HDT)
Great surface quality
Very good chemical resistance (bases, alcohols, oils, salts)

Material properties:

Material:	Polyamide 12 Carbon Fiber
Filament Sizes:	5.0 kg
Diameter:	2.85 mm
Density:	1.06 g/cm³
Flexural Modulus (ISO 178):	3500 MPa
Tensile Strength (ISO 527):	71 MPa
Impact Strength, notched (ISO 179):	12.5 kJ/m²
Heat Resistance HDT / B (ISO 75):	130 °C

Recommended printing conditions:

Nozzle Temperature:	270 - 300 °C
Print Bed Temperature:	>40-60 °C
Environmental Temperature:	n.a.
Printing Speed:	> 30-60mm/s

Specifications Safety Sheet

More Products

BVOH

Soporte hidro-soluble avanzado

Compatibility:

PRO STUDIO PRO

BigRep's BVOH support material is an ecologically friendly advanced water-soluble filament that eliminates post-processing for 3D printed parts. Created for use with dual-extruder printers, BVOH can be used in tandem with any other material to provide efficient support. It has been optimized for improved melt flow, eliminating concerns of hotend clogging that come with other soluble filaments.

Due to BVOH's ability to support heavy prints and the support-removal post-processing it eliminates, it's ideal for printing complex, ready-to-use prototypes and objects with large overhang or otherwise complex geometries.

BVOH easily dissolves in water - dissolving faster in higher temperatures - cleanly freeing parts from support structures without manual post-processing.

HIGHLIGHTS:

Water-soluble
Supports heavy prints
Nontoxic
Odorless

Physical properties:

Material:	Butenediol vinyl alcohol copolymer
Filament Sizes:	750g, 2.5 and 4.5kg (8.0 kg on request
Diameter:	2.85 mm
Density:	1.14 g/cm³
Flexural Modulus (ISO 178):	2200 MPa
Tensile Strength (ISO 527):	34 MPa
Young's Modulus (ISO 527):	78 MPa
Vicat Softening Temp (ISO 306):	≺60 °C

Recommended printing conditions:

Nozzle Temperature:	190 °C
Print Bed Temperature:	60 °C
Environmental Temperature:	n.a.
Printing Speed:	>30 mm/s

Additional comment: Material is sensitive to moisture and should be stored in dry conditions at all times.

ONLINE SHOP

More Products

ASA

Resistente a la intemperie y a los rayos UV

Compatibility:

PRO

BigRep ASA is an engineering-grade UV-resistant filament for high-strength and environmentally exposed applications. Designed for industrial and end-use parts, ASA is a strong material with high mechanical resistance, low shrinkage and superior layer adhesion. It is highly suited to applications in automotive, sporting goods, white goods and consumer appliances.

BigRep ASA has been optimized for large-format additive manufacturing and is able to print complex, ready-to-use parts including end-use, factory tooling and functional prototypes with demanding geometries.

HIGHLIGHTS:

High impact strength
High weather and UV resistance
Minimal shrinkage
High heat deflection temperature
Easy post-processing

Physical properties:

Material:	Acrylonnitrile Styrene Acrylatel
Filament Sizes:	2.3, 4.5 and 8.0 kg
Diameter:	2.85 mm
Density:	1.08 g/cm³
Flexural Modulus (ISO 178):	1250 MPa
Tensile Strength (ISO 527):	40 MPa
Tensile Modulus (ATM D638):	1900 MPa
Impact Strength, notched (ISO 179):	30 kJ/m³
HDT / B (ISO 750):	86 °C

Recommended printing conditions:

Nozzle Temperature:	200 - 240 °C
Print Bed Temperature:	40 - 80 °C
Environmental Temperature:	n.a.
Printing Speed:	> 40 mm/s

Additional comment: To ensure constant material properties and printability the filament should always be kept dry.

Specifications Safety Sheet

ONLINE SHOP

More Products

HI-TEMP CF

Fibra de carbono de alta temperatura

Compatibility:

PRO PRO

BigRep's HI-TEMP CF is a high-strength engineering-grade filament with a high heat deflection temperature. Highly stiff and incredibly durable, the material effectively maintains its form under high heat conditions. Ideal for the thermoforming process, HI-TEMP CF is the perfect match for the production of patterns and molds. With an excellent combination of heat - rivaling ASA - and durability, it's also ideal for functional applications regularly exposed to heat, like in the automotive or automation industries.

A reliable and easy-to-use material, BigRep HI-TEMP CF is optimized for large-format 3D printing and suitable for environments with limited control like factory floors.

HIGHLIGHTS:

Stiff and durable parts
Lightweight
Heat deflection temperature of up to 115 °C
Class A surface finish
Low moisture absorption

Physical properties:

Material:	BioPolymer with carbon fibre
Filament Sizes:	2.3, 4.5 and 8.0 kg
Diameter:	2.85 mm
Density:	1.20 g/cm³
Flexural Modulus (ISO 178):	7000 MPa
Tensile Strength (ISO 527):	65 MPa
Impact Strength, notched (ISO 179):	4.5 kJ/m³
Heat Resistance HDT / B (ISO 750):	115 °C
Hardness (Shore): (ISO 750):	n.a.

Recommended printing conditions:

Nozzle Temperature:	200 - 250 °C
Print Bed Temperature:	> 60 °C
Environmental Temperature:	n.a.
Printing Speed:	> 40 mm/s

Specifications Safety Sheet

ONLINE SHOP

More Products

PRO HT

Pro HT

Easy Printing and Support Removal

Compatibility:

PRO STUDIO

BigRep's Pro HT is a general-use bio performance material for open-environment 3D printing.

With a softening resistance up to 115 °C, it has a significant increase in temperature resistance compared to the average PLA; making it ideal for practical, end-use applications.

With increased temperature resistance, minimal warping and shrinking, Pro HT is an idea PLA alternative and the choice material for wearables or any general purpose product that may face higher than average temperatures.

Easy printing and support removal make finishing Pro HT parts simple and excel in low-volume additive manufacturing, even for end use. The material is scale dynamic, allowing designs to maintain their quality between large-format and desktop 3D printers.

As a material derived from organic compounds, Pro HT is biodegradable under the correct conditions. CO2 neutral and environmentally friendly, it has a much lower ecological impact than other plastics derived from fossil fuels.

Pro HT is FDA compliant for food safety and meets all requirements of EU Directives on food contact.

Hightlights:

Heat resistance up to 115 °C
Low warping and shrinkage
Easy printing and support removal
Environmentally Friendly Thermoplastic
Food Safe

Physical Properties:

Material:	BioPolymer
Filament Net Weight:	2.5 / 4.5 / 8.0 Kg
Diameter:	1.75 / 2.85 mm
Density:	1.3 g/cm³
Young's Modulus (ISO 527):	3.300 MPa
Tensile Strength (ISO 527):	44 MPa
Breaking Stress (ISO 178):	18 MPa
Vicat Softening Temp (ISO 306):	115 °C
HDT / B (ISO 75):	47 °C

Recommended Printing Conditions:

Nozzle Temperature:	195 - 205 °C
Print Bed Temperature:	55 - 60 °C
Environmental Temperature:	n.s. °C
Printing Speed:	>40 mm/s

Specifications Safety Sheet

SHOP GLOBAL

SHOP US & CANADA

Hi Temp

High-Temperature Resistant

Compatibility:

PRO STUDIO

BigRep's Hi-Temp is an ecological engineering-grade 3D printing filament for a wide variety of industrial and general applications.

It is resistant to high temperatures, maintaining a constant resistance up to 160 °C with minimal warping.

With such high heat resistance and an appealing matte surface finish, Hi-Temp filament is the choice for functional prototyping, household appliances, electrical casings, and as an end-use material for low-scale production or custom jigs and fixtures.

Hi-Temp is a scale dynamic, allowing designs to maintain their quality between large-format and desktop 3D printers. Compatible with open printers like the BigRep ONE, Hi-Temp is an excellent ABS alternative that is easily printable in low-temperature environments.

As a thermoplastic material derived from organic compounds, Hi-Temp is biodegradable under the correct conditions. CO2 neutral and environmentally friendly, it has a much lower ecological impact than other thermoplastics derived from fossil fuels - like ABS.

Hi-Temp is FDA compliant for food safety and meets all requirements of EU Directives on food contact.

HIGHLIGHTS:

Heat Resistance up to 160 °C
Low Warping and Shrinkage
Environmentally Friendly Thermoplastic
Appealing Matte Finish
Food Safe

Physical properties:

Material:	BioPolymer
Filament Sizes:	4.5 / 8.0 Kg
Diameter:	2.85 mm
Density:	1.39 g/cm³
Tensile Strength (ISO 527):	61 MPa
Young's Modulus (ISO 527):	4400 MPa
Breaking Stress (ISO 178):	50 MPa
Vicat Softening Temp (ISO 306):	160 °C
HDT/B (ISO 75):	115 °C

Recommended printing conditions:

Nozzle Temperature:	215 °C
Print Bed Temperature:	55 - 60 °C
Environmental Temperature	n.s. °C
Printing Speed	>40 mm

Additional comment: Material is sensitive to moisture and should be stored in dry conditions at all times.

Specifications Safety Sheet

SHOP GLOBAL

SHOP US & CANADA

PLA

Affordable and Versatile

BigRep PLA is an easy-to-use filament optimized for producing prototypes and pattern making, for end-use parts to the wide range of tooling applications.

Compatibility:

PRO STUDIO

The strength and stiffness of BigRep PLA makes this filament ideal for demanding industrial production, such as in 3D printing large objects for the architecture or construction fields.

PLA at a glance:

High level of strength
Extrudes very well between 190°C and 225°C
Low moisture absorption
Low warping
Naturally transparent (colors available)
Reduced environmental impact

BENEFITS & FEATURES

SPECIFICATIONS

BENEFITS & FEATURES

PLA can be printed at low to moderate temperatures and high speeds, and compared to other polymers used for 3D printing, the filament demonstrates minimal warping. Optimized for BigRep large-scale 3D printers, BigRep PLA enables successful prints without a special cooling system.

The mechanical behavior of BigRep PLA is suitable for most applications, though for applications requiring suitability with higher humidity (above 98%) and higher temperatures (above 60°C) other polymers should be used, such as PRO HT and PETG.

SPECIFICATIONS

Filament Net Weight:	2.5 / 4.5 / 8.0 Kg
Material:	Polylactic Acid (PLA)
Density:	1.24 g / cm³
Diameter:	2.85 mm
Print Temperature Guideline:	205 ° C
Heating Bed:	60 ° C
VST (ISO 306 VST A 120):	60 ° C
Tensile Strength (ISO 527):	60 MPa
Impact Strength (ISO 179):	7.5 KJ / m2
Flexural Modulus (ISO 178):	3800 MPa

Specifications Safety Sheet

SHOP GLOBAL

SHOP US & CANADA

PA6/66

Light-Weight and Resistant

Compatibility:

PRO

BigRep's PA6/66 is a highly durable 3D printing filament for industrial applications.

It is a light-weight thermoplastic material with high rigidity, and has high resistance to heat and chemicals. Its high compatibility with machining and mechanical strength make it an excellent candidate for most industrial applications, especially in the automotive and aerospace sectors.

Functionally similar to Nylon PA6, a common material for injection molding, PA6/66 is ideal for printing end-use parts or prototyping with nearly identical material properties to final, mass produced parts. The material's durability and production scalability make it the choice for not just industrial transportation applications, but also developing product electrical housing, cooling and heating systems, as well as molds and vacuum forming.

Prototyping with PA6/66 in full-scale with the same material properties as a final product can present substantial shortcuts in the product development cycle, circumventing frequent late stage iteration problems and dodging related exorbitant expenses.

Highlights:

Heat Resistance up to 180° C
Chemical Resistance
High Mechanical Strength
Low-Weight Products
Easily Machined

Physical properties:

Filament Sizes:	3.0 / 4.5 / 8.0 Kg
Density:	1.12 g/cm³
Tensile Strength (ISO 527):	67 MPa
Young's Modulus (ISO 527):	2325 MPa
Bending Modulus (ISO 178):	1725 MPa
Vicat Softening Temp (ISO 306):	180 °C

Recommended printing conditions:

Nozzle Temperature:	250 - 270 °C
Print Bed Temperature:	0 - 75 °C
Environmental Temperature:	40 - 60 °C
Printing Speed:	>40 mm

Specifications Safety Sheet

SHOP GLOBAL

SHOP US & CANADA

petg

PETG

Durable and Impact-Resistant

BigRep PETG is ideal for 3D printing projects requiring strength, toughness and thermal resistance in a filament.

Compatibility:

PRO STUDIO

The material is full compatible with all FFF open-build 3D printers, and has been optimized for use on BigRep large-scale machines, for a wide range of applications.

PETG at a glance:

High printing speed
Thermal resistant
Extrudes between 190-240°C
Minimal shrinkage and warping effect
Strong first-layer adhesion to heated print bed
Odorless

BENEFITS & FEATURES

SPECIFICATIONS

BENEFITS & FEATURES

PETG is a suitable alternative to PLA or ABS, depending on requirements, as it possesses excellent strength, toughness and temperature resistant properties. BigRep PETG extrudes odorlessly and readily achieves a smooth flow at temperatures from 215°C to 250°C, lending a glassy sheen to the transparent prints.

SPECIFICATIONS

Filament Net Weight:	2.3 Kg
Material:	PolyEthylene Terephthalate Glycol
Density:	1.27 g/cm³
Diameter:	2.85 mm
Print Temperature Guideline:	205 - 220 °C
Heating Bed:	80 °C
VST (ISO 306 VST A 120):	70°C
Tensile Strength (ISO 527):	50 MPa
Impact Strength (ISO 179):	7.2 KJ/m²
Flexural Modulus (ISO 178):	2145 MPa

Specifications Safety Sheet

SHOP GLOBAL

SHOP US & CANADA

ACERCA DE NOSOTROS

INDUSSTRIAS

PA12 CF

Fiber Fibra de carbono rígida y resistente

HIGHLIGHTS:

Material properties:

Recommended printing conditions:

More Products

BVOH

Soporte hidro-soluble avanzado

HIGHLIGHTS:

Physical properties:

Recommended printing conditions:

More Products

ASA

Resistente a la intemperie y a los rayos UV

HIGHLIGHTS:

Physical properties:

Recommended printing conditions:

More Products

HI-TEMP CF

Fibra de carbono de alta temperatura

HIGHLIGHTS:

Physical properties:

Recommended printing conditions:

More Products

Pro HT

Easy Printing and Support Removal

BigRep's Pro HT is a general-use bio performance material for open-environment 3D printing.

Hightlights:

Physical Properties:

Recommended Printing Conditions:

Hi Temp

High-Temperature Resistant

BigRep's Hi-Temp is an ecological engineering-grade 3D printing filament for a wide variety of industrial and general applications.

HIGHLIGHTS:

Physical properties:

Recommended printing conditions:

PLA

Affordable and Versatile

BigRep PLA is an easy-to-use filament optimized for producing prototypes and pattern making, for end-use parts to the wide range of tooling applications.

The strength and stiffness of BigRep PLA makes this filament ideal for demanding industrial production, such as in 3D printing large objects for the architecture or construction fields.

PLA at a glance:

PA6/66

Light-Weight and Resistant

BigRep's PA6/66 is a highly durable 3D printing filament for industrial applications.

Highlights:

Physical properties:

Recommended printing conditions:

PETG

Durable and Impact-Resistant

BigRep PETG is ideal for 3D printing projects requiring strength, toughness and thermal resistance in a filament.

The material is full compatible with all FFF open-build 3D printers, and has been optimized for use on BigRep large-scale machines, for a wide range of applications.

PETG at a glance: